白桦树盘生长特性对干燥开裂的影响

doi:10.11707/j.1001-7488.20130719

摘要/Abstract

摘要：

以白桦树盘为对象,研究分别采用恒温40、60℃,相对湿度渐降的干燥工艺干燥时,树盘干燥开裂的特点(产生时期、部位、形貌),进而研究树盘几何生长特性(偏心率、圆度、横截面积)对干燥开裂的影响。结果表明: 树木不同部位、不同径级、不同圆度的树盘,在相同干燥工艺下开裂初期差异很大。开裂初期均值,在40℃干燥工艺下对应树盘含水率43.9%,60℃干燥工艺下对应树盘含水率45.6%,温度高时平均开裂期超前; 最初开裂产生位置大多为心边材交界处,60℃工艺时有向内扩张趋势,并伴有心裂产生; 60℃干燥工艺下无论开裂总长度还是平均开裂宽度都要较40℃工艺时的开裂值大,但差异不显著; 60℃工艺时的V-裂数量明显高于40℃时; 圆度与橫截面积是影响开裂总长度、开裂平均宽度的主要影响因素,而V-裂主要受后者影响。横截面积越大、形状越不规则,树盘越易产生干燥开裂,揭示树盘按几何生长特征分选干燥的必要性。

关键词: 白桦, 树盘, 几何生长特性, 干燥, 开裂

Abstract:

This paper was carried out to study the characteristics of white birch (Betula platyphylla) disk drying checks(such as the position, MC of check formation, morphology)under stepwise decreasing relative humidity and constant temperature of 40 and 60℃ drying conditions. On that basis, the effects of geometrical characteristics of tree disk, namely, growth eccentricity(GE), roundness deviation(RD)and cross-sectional area(S)on drying checks were investigated. The results showed that under the same drying condition, the early formation of checks within disks with different position, diameter and roundness deviation(RD)had a significant difference. Under 40℃ and 60℃ drying conditions, the early formation of checks' average MC value was 43.9% and 45.6%, respectively. The occurrence of checks was earlier under 60℃ than 40℃ drying condition. Also, the early formation of checks' position was on the border between heartwood and sapwood. Under 60℃ drying condition, the position of checks was slightly expansion to inter with heart checks emerging. Although check total length(CTL)and check average width(CAW)under 60℃ were greater than 40℃ drying condition, there was no significant difference under two drying conditions. The number of V-checks was under 60℃ more than 40℃ drying condition, obviously. The roundness deviation(RD)and cross-sectional area (S)were the main factors that effected check total length and V-check. The disks with larger cross-sectional area(S)and more irregular shape were prone to triggering drying checks during the drying process. Therefore, it was necessary that tree disks were sorted by geometrical characteristics prior to drying.

Key words: white birch, disk, geometrical characteristics, drying, check

中图分类号:

S782.31

赵景尧, 蔡英春, 付宗营. 白桦树盘生长特性对干燥开裂的影响[J]. 林业科学, 2013, 49(7): 129-135.

Zhao Jingyao, Cai Yingchun, Fu Zongying. Effect of White Birch Disk Characteristics on Drying Check Behaviors[J]. Scientia Silvae Sinicae, 2013, 49(7): 129-135.

参考文献

艾沐野,张晓峰,朱政贤,等. 1996. 白桦小径木截片干燥技术的研究. 木材工业, 10(3):13-15.

成俊卿.1985.木材学.北京: 中国林业出版社.

刘一星,赵广杰.2004.木质资源材料学.北京: 中国林业出版社.

孟祥柏,蒋福来,孙品,等.1991.小径木橫截片干燥工艺初探.林业科技, 16(6):37-38.

帕夫利迪斯.1987.计算机图形显示和图象处理的算法.北京: 科学出版社.

王丽宇,曲艳杰,朱政贤,等. 1998. 硕桦小径木圆截片常规干燥工艺初探. 北京林业大学学报,20(3):89-92.

王丽宇. 1998. 刺槐小径木圆、斜截片微波干燥技术. 北京林业大学学报,20(5):103-107.

王喜明,高志悦,安珍,等. 1998. 改性白桦小径木横截片干燥特性的研究. 木材工业, 12(1):14-18.

杨亮庆.2011. 枫桦圆盘预处理及干燥特性研究.哈尔滨:东北林业大学博士学位论文.

Brooke A S, Langrish T A G. 1997. The simulation of stresses and strains in the drying of Pinus radiata sapwood: the effects of board geometry. Computers & Chemical Engineering, 21(11):1271-1281.

Brunner R. 1987. Die schnittholztrocknung. Buchdruckwerkstätten Hannover Gmbh, Hannover.

Flæte P O, Høibø O A, Fjærtoft F, et al. 2000. Crack formarion in unfinished siding of aspen(Populus tremula L.)and Norway spruce(Picea abies(L.)Karst.)during accelerated weathering. Holz als Roh-und Werkstoff, 58(3):135-139.

Ilic J. 1999. Shrinkage-related degrade and its association with some physical properties in Eucalyptus regnans F.Muell. Wood Science and Technology, 33(5):425-437.

Kang W, Lee N H. 2002. Mathematical models to predict drying deformation and stress due to the differential shrinkage within a tree disk with radial variations. Wood Sci Technol,36(6):463-476.

Kang W, Lee N H, Choi J H. 2004a. A radial distribution of moistures and tangential strains within a larch log cross section during radio-frequency/vacuum drying. Holz als Roh-und Werkst,62(1):59-63.

Kang W, Lee N H.2004b. Relationship between radial variations in shrinkage and drying defects of tree disks. J Wood Sci, 50(3):209-216.

Kato H, Sadoh T, Matsui K, et al. 1978. Shrinkage and crack formation of cross-sectional tree-disks. Bull Kyoto Univ For, 50:191-197.

Kubler H.1974a. How to cut tree disks without formation of checks. Forest Products Journal, 24:57-59.

Kubler H. 1974b. Drying tree disks simply and without defects. Forest Products Journal, 24:33-35.

Kubler H. 1975. Study on drying of tree cross sections. Wood Sci, 7:173-181.

Lagana R, Dizhbite T, Telysheva G, et al.2006. An influence of thermal treatment on surface properties of wood. Conference of Wood Structure and Properties, Zvolen, Slovakia, 289-291.

Li C Y, Lee N H. 2007. Effect of external compressive load on tangential strain behavior in Japanese larch log cross sections duringradio-frequency/vacuum drying. J Wood Sci,53(4):291-295.

Li C Y, Lee N H. 2004. Effect of compressive load on shrinkage of larch blocks underradio-frequency/vacuum heating. Wood Fiber Sci,36(1):9-16.

Lee N H, Hayashi K, Jung H S. 1998. Effect ofradio-frequency/vacuum drying and mechanical press-drying on shrinkage and checking of walnut log cross sections. Forest Prod J,48(5):73-79.

Lee N H, Li C Y, Choi J H, et al. 2004. Comparison of moisture distribution along radial direction in a log cross section of heartwood and mixed sapwood and heartwood duringradio-frequency/vacuum drying. J Wood Sci, 50(6):484-489.

Mugabi P, Rypstra T, Vermaas H F, et al. 2009. Relationships between drying defect parameters and some growth characteristics in kiln-dried South African grown Eucalyptus grandis poles. Eur J Wood Prod, 68(3):329-340.

Oltean L, Teischinger A, Hansmann C. 2007. Influence of temperature on cracking and mechanical properties of wood duringdrying-a review. BioResources, 2(4): 789-811.

Schniewind A P. 1963. Mechanism of check formation. Forest Prod J,13: 475-480.

Yamashita K, Hirakawa Y, Nakatani H. 2009. Tangential and radial shrinkage variation within trees in sugi (Cryptomeria japonica)cultivars. J Wood Sci,55(3):161-168.

Yang L Q, Liu Y X, Cai Y C, et al. 2011. Drying characteristics of birch tree disk impregnated with NaCl. Advanced Material Research,(179/180):285-288.

Youngs R L. 1957. The perpendicular-to-grain mechanical properties of red oak as related to temperature, moisture content, and time. Report 2079. U.S. Forest Products Laboratory, Madison,Wis.

Zhou J, Shen J. 2003. Ellipse detection and phase demodulation for wood grain orientation measurement based on the tracheid effect. Optics and Lasers in Engineering, 39(1):73-89.

[1]	金明月, 姜峰, 金光泽, 刘志理. 不同年龄白桦比叶面积的生长阶段变异及冠层差异[J]. 林业科学, 2018, 54(9): 18-26.
[2]	王哲, 王喜明. 活立木生理干燥过程中水分传输和散失机制探讨[J]. 林业科学, 2018, 54(3): 123-133.
[3]	侯俊峰, 鲍永泽, 周永东. 过热蒸汽预处理对50 mm厚杨木锯材常规干燥的影响[J]. 林业科学, 2018, 54(2): 131-136.
[4]	马尔妮, 王望, 李想, 杨甜甜. 基于LFNMR的木材干燥过程中水分状态变化[J]. 林业科学, 2017, 53(6): 111-117.
[5]	鲍咏泽, 周永东. 柳杉锯材过热蒸汽干燥与常规干燥的比较[J]. 林业科学, 2017, 53(1): 88-93.
[6]	刘宇, 徐焕文, 尚福强, 焦宏, 张利民, 罗建新, 滕文华, 刘桂丰. 16年生白桦种源变异及区划[J]. 林业科学, 2016, 52(9): 48-56.
[7]	李贵雨, 卫星, 汤园园, 吕琳, 杜欣竹. 白桦不同轻基质容器苗生长及养分分析[J]. 林业科学, 2016, 52(7): 30-37.
[8]	李永宁, 刘丽颖, 冯楷斌, 黄选瑞. 燕山北部白桦林剥皮木的空间分布特征及风折规律[J]. 林业科学, 2016, 52(1): 10-17.
[9]	王冬至, 张冬燕, 张志东, 黄选瑞. 基于非线性混合模型的针阔混交林树高与胸径关系[J]. 林业科学, 2016, 52(1): 30-36.
[10]	董晓璐, 孙耀星, 杜洪双, 赵雪, 蒋涛. 辊压预处理条件对蒙古栎干燥速率及纹孔结构的影响[J]. 林业科学, 2015, 51(1): 103-111.
[11]	张明辉, 李新宇, 周云洁, 高玉磊. 利用时域核磁共振研究木材干燥过程水分状态变化[J]. 林业科学, 2014, 50(12): 109-113.
[12]	周永东, 孙锋, 吕建雄, 李晓玲. 6种桉木单板干燥质量的比较[J]. 林业科学, 2014, 50(11): 104-108.
[13]	苗虎, 周玉成, 侯晓鹏, 刘鑫钰, 安源, 张国梁. 木材除湿干燥模糊控制系统的设计与实现[J]. 林业科学, 2014, 50(10): 99-105.
[14]	孙美玲, 李晓灿, 王晓东, 詹亚光, 范桂枝. H₂O₂介导真菌诱导子促进白桦酯醇积累[J]. 林业科学, 2013, 49(7): 57-61.
[15]	赵西平, 郭平平, 张全智. 白桦枝叶的空间分布及导管特征[J]. 林业科学, 2013, 49(7): 69-74.