林业科学 ›› 2010, Vol. 46 ›› Issue (12): 125-129.doi: 10.11707/j.1001-7488.20101221

• 论文 • 上一篇    下一篇

物理法制备炭陶复合吸附材料及其表征

林冠烽1, 黄彪2, 陈学榕2, 廖益强2, 唐丽荣2, 曾巧玲2   

  1. 1. 福建省林业科学研究院 福州 350012;2. 福建农林大学材料工程学院 福州 350002
  • 收稿日期:2009-06-29 修回日期:2009-08-28 出版日期:2010-12-25 发布日期:2010-12-25
  • 通讯作者: 黄彪

Preparation and Characterization of Carbon/Pottery Composite with Physical Method

Lin Guanfeng1, Huang Biao2, Chen Xuerong2, Liao Yiqiang2, Tang Lirong2, Zeng Qiaoling2   

  1. 1. Fujian Academy of Forestry Fuzhou 350012;2. College of Material Engineering,Fujian Agriculture and Forestry University Fuzhou 350002
  • Received:2009-06-29 Revised:2009-08-28 Online:2010-12-25 Published:2010-12-25

摘要:

以木炭和黏土为原料,采用物理法制备炭陶复合吸附材料,讨论温度和保温时间对其吸附性能的影响,采用扫描电镜(SEM)和全自动比表面积及孔径分析仪对其微观结构和孔径分布进行表征,提出原位活化的思路。结果表明: 热处理过程中,木炭的收缩在木炭和陶土之间形成发达的孔隙; 黏土在烧结之后并没堵塞活性炭的孔隙结构; 块状炭陶的吸附性能比粉状的高; 炭陶在制备过程中受原位活化作用。在较优的工艺条件下,炭陶复合吸附材料的亚甲基蓝吸附值和碘吸附值分别为127.5和543.6 mg ·g-1

关键词: 炭陶复合材料, 孔径分布, 原位活化, 活性炭

Abstract:

The preparation of carbon/pottery composite from wood charcoal and clay was made with physical method and the effect of temperature and holding time on the adsorption capability of carbon/pottery composite was discussed in this paper. In addition, microstructure and pore distribution of carbon/pottery composite were characterized by SEM and BET and the idea of in situ activation was proposed.The results show the pore between wood charcoal and pottery developed during heating treatment while the clay did not block the pore structure of wood charcoal. On the other hand, the adsorption capability of lumpish shape was higher than pulverous shape. Furthermore, the activated reaction of carbon/pottery composite could be defined as in situ activation.Therefore, under optimized experimental condition,the adsorption values of methylene blue and iodine of carbon/pottery composite were 127.5 and 543.6 mg ·g-1 respectively.

Key words: carbon/pottery composite, pore distribution, in situ activation, activated carbon