天府农博园主展馆GL24h欧洲云杉胶合木力学性质试验探究

doi:10.11707/j.1001-7488.LYKX20240468

Abstract

Abstract:

Objective: In response to the differences between the mechanical property testing methods, testing environments, and wood structure design methods of imported glued laminated timber (GLT) and China's standard specifications, a study was conducted on the mechanical property testing of imported GLT. The typical loading characteristics and failure modes of various specimens were summarized, and the strength standard values were determined to provide reference for the determination of strength design values of imported GLT. Method: Taking the GL24h European spruce (Picea abies) GLT used in the main exhibition hall of Tianfu Agricultural Expo Park as the object, the loading characteristics and failure mode of its raw materials were explored through small clear specimen mechanical tests. Based on the improvement of the current standard method, the strength standard value and design value of GL24h were determined and compared with the European standard EN 14080: 2013 and the“Standard for design of Timber structures”(GB 50005—2017), respectively. Result: Research has shown that the characteristic value of radial compressive strength of GL24h provided by EN 14080: 2013 is 4.60% higher than the experimental value, while the longitudinal compressive strength is 20.27% lower, and the longitudinal tensile strength, bending strength, elastic modulus, and radial shear strength are all about 50% lower. The design value of longitudinal compressive strength, radial compressive strength, longitudinal tensile strength, bending strength, and radial shear strength of GL24h determined by GB 50005—2017 were 9% higher than that determined by the improved γ_R-V_R envelope curve. Conclusion: When the load conditions where the timber structure building is located are known, a more accurate strength design values of imported timber can be calculated according to the reliability analysis results in the GB 50005—2017, combined with the actual load conditions. It is still necessary to further improve the method for determining the design value of strength of imported GLT.

Key words: Tianfu Agricultural Expo Park, imported glued laminated timber, design value of strength, mechanical tests, partial coefficient of resistance

CLC Number:

Zhongcheng Wang,Jiulin Li,Na Yang,Yinghui Yang,Ziliang Miao,Yongliang Sun. Exploration of Mechanical Properties of GL24h European Spruce Glued Laminated Timber in the Main Exhibition Hall of Tianfu Agricultural Expo Park[J]. Scientia Silvae Sinicae, 2025, 61(9): 184-194.

Figures/Tables 17

Table 1

Fig.1

Fig.2

Fig.3

Fig.4

Fig.5

Fig.6

Fig.7

Fig.8

Fig.9

Fig.10

Table 2

Table 3

Table 4

Fig.11

Fig.12

Table 5

References 0

	柳炳康. 2003. 荷载与结构设计方法. 武汉: 武汉理工大学出版社.
	Liu B K. 2003. Load and structural design methods. Wuhan: Wuhan University of Technology Press. ［in Chinese］
	龙卫国. 2021. 木结构设计手册. 4版. 北京: 中国建筑工业出版社.
	Long W G. 2021. Design manual of timber structure. 4th ed. Beijing: China Architecture & Building Press. ［in Chinese］
	陆伟东, 杨会峰, 刘伟庆, 等. 胶合木结构的发展、应用及展望. 南京工业大学学报(自然科学版), 2011, 33 (5): 105- 110.
	Lu W D, Yang H F, Liu W Q, et al. Development, application and prospects of glulam structures. Journal of Nanjing Tech University (Natural Science Edition), 2011, 33 (5): 105- 110.
	乔　梁. 2015. 木结构可靠度分析及木产品强度设计指标的确定方法. 哈尔滨: 哈尔滨工业大学.
	Qiao L. 2015. Reliability analysis of timber structures and method for determining the strength design value of wood products. Harbin: Harbin Institute of Technology. ［in Chinese］
	王永维. 概率极限状态设计方法及在木结构设计规范中的应用(一). 四川建筑科学研究, 1982a, (1): 40- 46.
	Wang Y W. Probabilistic limit state design method and its application in the design code for timber structures (Part 1). Sichuan Building Science, 1982a, (1): 40- 46.
	王永维. 概率极限状态设计方法及在木结构设计规范中的应用(二). 四川建筑科学研究, 1982b, (2): 64- 73.
	Wang Y W. Probabilistic limit state design method and its application in the design code for timber structures (Part 2). Sichuan Building Science, 1982b, (2): 64- 73.
	王永维. 概率极限状态设计方法及在木结构设计规范中的应用(三). 四川建筑科学研究, 1982c, (3): 73- 80, 47.
	Wang Y W. Probabilistic limit state design method and its application in the design code for timber structures (Part 3). Sichuan Building Science, 1982c, (3): 73- 80, 47.
	王永维. 概率极限状态设计方法及在木结构设计规范中的应用(四). 四川建筑科学研究, 1982d, (4): 28- 31, 14.
	Wang Y W. Probabilistic limit state design method and its application in the design code for timber structures (Part 4). Sichuan Building Science, 1982d, (4): 28- 31, 14.
	王永维. 概率极限状态设计方法及在木结构设计规范中的应用(五). 四川建筑科学研究, 1983, (1): 63- 66.
	Wang Y W. Probabilistic limit state design method and its application in the design code for timber structures (Part 5). Sichuan Building Science, 1983, (1): 63- 66.
	许佳乐, 邬　沛, 唐政烽, 等. 钢-单板层积材组合工字形梁受弯性能试验. 森林工程, 2024, 40 (6): 185- 195. doi: 10.7525/j.issn.1006-8023.2024.06.019
	Xu J L, Wu P, Tang Z F, et al. Experimental study on flexural properties of steel-LVL composite I-beams. Forest Engineering, 2024, 40 (6): 185- 195. doi: 10.7525/j.issn.1006-8023.2024.06.019
	杨　娜, 王忠铖, 常　鹏. 藏青杨旧材无疵试样力学性能试验研究. 建筑结构学报, 2022, 43 (11): 168- 176.
	Yang N, Wang Z C, Chang P. Experimental study on mechanical properties of small clear specimens of aged Tibetan populus cathayana. Journal of Building Structures, 2022, 43 (11): 168- 176.
	张　雷. 2017. 木材的力学性质试验研究及数值模拟方法. 北京: 北京交通大学.
	Zhang L. 2017. Experimental study on the mechanical properties of wood and the numerical modeling strategies of wood. Beijing: Beijing Jiaotong University. ［in Chinese］
	周先雁, 曹　磊, 周佳乐, 等. 胶合木设计制作与质量控制. 中南林业科技大学学报, 2014, 34 (12): 136- 140. doi: 10.3969/j.issn.1673-923X.2014.12.025
	Zhou X Y, Cao L, Zhou J L, et al. Design and fabrication of glulam timber and products quality control. Journal of Central South University of Forestry & Technology, 2014, 34 (12): 136- 140. doi: 10.3969/j.issn.1673-923X.2014.12.025
	祝恩淳, 牛爽, 乔梁, 等. 木结构可靠度分析及木材强度设计值的确定方法. 建筑结构学报, 2017, 38 (2): 9- 17.
	Zhu E C, Niu S, Qiao L, et al. Reliability analysis of wood structures and method for determining design strength value of timber. Journal of Building Structures, 2017, 38 (2): 9- 17.
	祝恩淳, 潘景龙. 2011. 借鉴国际先进经验制(修)定我国木结构技术标准. 木材工业, 25(3): 4−7.
	Zhu E C, Pan J L. 2011. Improving technical standards for wood structures with reference to international experience, China Wood Industry, 25(3): 4−7. ［in Chinese］
	Barrett J D, Lau W. 1994. Canada lumber properties. Ottawa: Canadian Wood Council.
	Benabou L, Sun Z. Numerical study of anisotropic failure in wood under large deformation. Materials and Structures, 2015, 48 (6): 1977- 1993. doi: 10.1617/s11527-014-0287-6
	Byskov E, Christoffersen J, Dencker Christensen C, et al. Kinkband formation in wood and fiber composites: morphology and analysis. International Journal of Solids and Structures, 2002, 39 (13/14): 3649- 3673.
	Foschi R O, Folz B R, Yao F Z. 1989. Reliability-based design of wood structures. Canada: First Folio Printing Corp. Ltd.
	Pimenta S, Gutkin R, Pinho S T, et al. A micromechanical model for kink-band formation: Part II: analytical modelling. Composites Science and Technology, 2009, 69 (7/8): 956- 964.
	Ranta-Maunus A, Fonselius M, Kurkela J, et al. 2001. Reliability analysis of timber structures. VTT Research Notes 2109.

试验类型 Test type	样本量 Sample size	气干密度 Air-dry density/(kg·m^?3)	含水率 Moisture content (%)	加载速率 Loading rate/(mm·min^?1)
顺纹抗压Longitudinal compression	42	410.93	12.64	0.6
横纹径向抗压 Transverse radial compression	40	424.52	12.69	1.0
顺纹抗拉Longitudinal tensile	28	—	12.33	3.0
抗弯Bending	34	426.26	10.63	3.0
径切面抗剪 Radial section shear	37	—	14.68	2.0

试验类型 Test type		顺纹抗压 Longitudinal compression	横纹径向抗压 Transverse radial compression	顺纹抗拉 Longitudinal tensile	抗弯 Bending	径切面抗剪 Radial section shear
比例极限强度 Proportional ultimate strength	均值 Mean value/MPa	17.71	1.62	40.28	25.35	4.60
	标准差 Standard deviation/MPa	2.53	0.26	7.94	2.17	0.34
	变异系数 Coefficient of variation	0.147 6	0.165 6	0.200 3	0.079 9	0.084 9
极限强度 Ultimate strength	均值 Mean value/MPa	32.31	2.94	73.61	49.40	7.55
	标准差 Standard deviation/MPa	4.50	0.30	17.66	4.10	0.43
	变异系数 Coefficient of variation	0.143 7	0.104 1	0.241 1	0.078 4	0.061 4
弹性模量 Elastic modulus	均值 Mean value/MPa	—	—	—	20 538.46	—
	标准差 Standard deviation/MPa	—	—	—	3 709.63	—
	变异系数 Coefficient of variation	—	—	—	0.176 9	—

强度指标 Strength index	极限强度 Ultimate strength/MPa	标准差 Standard deviation/MPa	K₁	标准值 Standard value/MPa
顺纹抗压 Longitudinal compression	32.31	4.50	1.828	24.08
横纹径向抗压 Transverse radial compression	2.94	0.30	1.834	2.39
顺纹抗拉 Longitudinal tensile	73.61	17.66	1.878	40.44
抗弯 Bending	49.4	4.10	1.853	41.80
径切面抗剪 Radial section shear	7.55	0.43	1.842	6.76

标准值对比 Comparison of standard values	强度 Strength/MPa					弹性模量 Elastic modulus/ MPa
标准值对比 Comparison of standard values	顺纹抗压 Longitudinal compression	横纹径向抗压 Transverse radial compression	顺纹抗拉 Longitudinal tensile	抗弯 Bending	径切面抗剪 Radial section shear	弹性模量 Elastic modulus/ MPa
试验值 Test value	24.08	2.39	40.44	41.8	6.76	19 457.47
欧洲规范GL24h GL24h in European standard	19.2 (?20.27%)	2.5 (4.60%)	19.2 (?52.52%)	24 (?42.58%)	3.5 (?48.22%)	9 600 (?50.66%)
国标TC_T18 TC_T18 in national standard	21 (?12.79%)	—	20 (?50.54%)	24 (?42.58%)	—	6 500 (?66.59%)

设计值对比 Comparison of design values	强度设计值Design value of strength/MPa					弹性模量 Elastic modulus/MPa
设计值对比 Comparison of design values	顺纹抗压 Longitudinal compression	横纹径向抗压 Transverse radial compression	顺纹抗拉 Longitudinal tensile	抗弯 Bending	径切面抗剪 Radial section shear	弹性模量 Elastic modulus/MPa
γ_R包络值 Envelope value of γ_R	1.398	1.375	1.861	1.416	1.562	—
包络设计值 Envelope design value	8.06	0.81	5.66	9.80	1.87	10 750.25
γ_R规范值 Standard value of γ_R	1.067	1.051	1.409	1.069	1.182	—
规范设计值 Standard design values	8.77（8.81%）	0.88（8.64%）	6.21（9.72%）	10.77（9.90%）	2.05（9.90%）	10 750.25

Exploration of Mechanical Properties of GL24h European Spruce Glued Laminated Timber in the Main Exhibition Hall of Tianfu Agricultural Expo Park

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 17

References 0

Related Articles 0

Recommended Articles

Metrics

Comments