导电功能木质复合板材的渗滤阈值

doi:10.11707/j.1001-7488.20010118

林业科学 ›› 2001, Vol. 37 ›› Issue (1): 117-120.doi: 10.11707/j.1001-7488.20010118

导电功能木质复合板材的渗滤阈值

傅峰¹ 吕斌³ 王志同⁴ 华毓坤²

中国林业科学研究院木材工业研究所,北京10091；南京林业大学木材工业学院,南京210037

收稿日期:1999-12-30 修回日期:1900-01-01 出版日期:2001-01-25 发布日期:2001-01-25

PERCOLATION THRESHOLD OF ELECTRICALLY CONDUCTIVE FUNCTION IN WOOD-BASED COMPOSITE PANELS

Fu Feng¹,Lü Bin³,Wang Zhitong⁴,Hua Yukun²

Research Institute of Wood Industry,CAF Beijing 100091;College of Wood Science and Technology,Nanjing Forestry University Nanjing 210037

Received:1999-12-30 Revised:1900-01-01 Online:2001-01-25 Published:2001-01-25

摘要/Abstract

摘要：

通过导电单元掺杂粘合单元并叠层复合木质单元研究了导电功能木质复合板材的渗滤阈值。结果表明,形成渗滤效应时的阈值为8%～14% ,对应的导电单元施加量和填充量分别约为14%～25%和12%～20%;形成渗滤效应之后,导电功能的均匀性较好。此外,相关机理和量化关系还有待于深入研究。

关键词: 渗滤阈值, 导电功能, 木质复合板材

Abstract:

The percolation threshold of electrically conductive function was studied by mixing adhesive elements with conductive elements and then laminating with wood elements together to form wood-based composite panels.The results showed that the threshold values were about 8%～14%,and the spreading content and filling content were correspondingly about 14%～25% and 12%～20%,respectively.The uniformity of conductive function was better once the percolation phenomena occurred.Additionally,some mechanism and numerical relationship should be further researched.

Key words: Percolation threshold, Electrically conductive function, Wood-based composite panels

傅峰吕斌王志同华毓坤. 导电功能木质复合板材的渗滤阈值[J]. 林业科学, 2001, 37(1): 117-120.

Fu Feng;Lü Bin;Wang Zhitong;Hua Yukun. PERCOLATION THRESHOLD OF ELECTRICALLY CONDUCTIVE FUNCTION IN WOOD-BASED COMPOSITE PANELS[J]. Scientia Silvae Sinicae, 2001, 37(1): 117-120.

导电功能木质复合板材的渗滤阈值

PERCOLATION THRESHOLD OF ELECTRICALLY CONDUCTIVE FUNCTION IN WOOD-BASED COMPOSITE PANELS

PDF

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics

本文评价

作者中心

期刊获奖

引证指标

联系方式